Standar: | JIS G4305, JIS G4304, ASTM A240 | Kelas Meterial: | SUS430J1L , SUS304 |
---|---|---|---|
Permukaan: | BA , 2B, LBA | Kekerasan: | 1/4H, 1/2H, 3/4H, H, FH |
Cahaya Tinggi: | SUS 430J1L Strip Stainless Steel,Strip Stainless Steel 3/4H,Strip Stainless Steel JIS G4305 |
JIS G4305 SUS 430J1L Strip Baja Tahan Karat, 3/4H, LBA, Dilindungi PVC
Yuhong Group sudah memasok strip baja tahan karat kami ke Sinagpore, Malasiya, Indonesia, Korea, UEA, Kolombia, .... Strip ss sudah lebar digunakan di Peralatan Dapur, hard disk komputer, rokok elektronik, semikonduktor, industri makanan, industri otomotif , ....Produk kami sesuai dengan ASTM A240 , JIS G4304, JIS 4305 , Permukaan menurut: 2B, BA, LP, Mirror, .... Tingkat kekerasan: 1/4H, 1/2H, 3/4H, H , FH .
Lembar Baja Tahan Karat ASTM 430J1L/ 1.4511Komposisi kimia | ||||||||||||
C | Ya | M N | P | S | Kr | Mo | Ti | Nb | Cu | Al | N | Ni |
0,025 | 1,00 | 1,00 | 0,04 | 0,03 | 16,0-20,0 | 8x(C+N)-0,8 | 0,3-0,8 | 0,025 |
Lembar Baja Tahan Karat ASTM 430J1L/ 1.4511Peralatan mekanis | ||||
Ylapangan | Tarik | Pemanjangan | Kekerasan, maks | |
Min Mpa | Mpa | Min % | Brinell | Rockwell B |
205 | 390 | 22% | 192 | 90 |
Permukaan Akhir dari kumparan stainless steel | |
Permukaan Selesai
|
Definisi dan Aplikasi |
No.1 | Permukaan diselesaikan dengan perlakuan panas dan pengawetan atau proses yang sesuai setelahnya setelah penggulungan panas |
2D | Selesai setelah pengerolan dingin, dengan perlakuan panas, pengawetan atau perlakuan setara lainnya |
2B | Selesai setelah pengerolan dingin, dengan perlakuan panas, pengawetan atau perlakuan setara lainnya dan terakhir dengan pengerolan dingin untuk memberikan kilau yang sesuai |
BA | Cold rolled, bright annealed dan skin-passed, produk ini memiliki kecerahan yang sangat baik dan refleksivitas yang baik seperti cermin |
NOMOR 3 | Dipoles dengan sabuk abrasif grit #100~#200, memiliki kecerahan lebih baik dengan stria kasar terputus-putus |
NO.4 | Dipoles dengan sabuk abrasif grit #150~#180, memiliki kecerahan lebih baik dengan stria kasar terputus-putus |
HL | Dipoles dengan abrasive belt of grit#150~#320 pada lapisan NO.4 dan memiliki goresan terus menerus |
8K | Produk memiliki kecerahan yang sangat baik dan refleksivitas prefek dapat menjadi cermin |
Jenis, Sifat Mekanis, Sifat Fisik
|
||||||||||||||
Jenis | Komposisi kimia (%) | Peralatan mekanis | Properti fisik | |||||||||||
KS(JIS) | POSCO | C | Kr | Ni | Mo | Yang lain | Kekuatan Hasil (0,2%) | Daya tarik | Perpanjangan (%) | Kekerasan (Hv) | Panas Spesifik J/g °C | Berat jenis | Koefisien Ekspansi Termal | Konduktivitas termal |
(N/mm²) | (N/mm²) | W/m·°C | W/m·°C | |||||||||||
(20-100°C) | (100°C) | |||||||||||||
409L | 409L | 0,03 | 10.50~ 11.75 | - | - | Ti 6xC%~0,75 | 175~ | 360~ | 25~ | ~175 | 0,46 | 7.75 | 6.5 | 24.9 |
- | HIPOS | ~0,03 | 12~14 | - | - | Si~1.3 | 175~ | 360~ | 22~ | ~180 | - | - | - | - |
410L | 410L | ~0,03 | 11.0~ 13.5 | - | - | - | 195~ | 360~ | 22~ | ~200 | 0,46 | 7.75 | 9.9 | 25.1 |
- | 429EM | 0,02 | 13.0~ 15.0 | - | - | Si~1.5 | 205~ | 400~ | 25~ | ~180 | 0,456 | 7.62 | 10.6 | 20.9 |
430 | 430 | ~0,12 | 16.0~ 18.0 | - | - | - | 205~ | 450~ | 22~ | ~200 | 0,46 | 7.7 | 10.5 | 23.9 |
430J1L | 430J1L | ~0,025 | 16.0~ 20.0 | - | - | N~0,025 | 205~ | 390~ | 22~ | ~200 | 0,46 | 7.7 | 10.4 | 26.2 |
430Ti | 430Ti | ~0,02 | 19,5~ 20,5 | - | - | Ti 0,3~0,6 | 206~ | 422~ | 25~ | ~180 | 0,46 | 7.7 | 10.4 | 26.4 |
436L | 436L | ~0,025 | 16.0~ 19.0 | - | 0,75~ 1,5 | Ti, Nb, Zr 8x(C%+N%)~0,8 | 245~ | 410~ | 20~ | ~230 | 0,46 | 7.7 | 9.3 | 23.9 |
- | 439 | 0,03 | 17.0~ 19.0 | - | - | Ti 0,2~1,0 | 175~ | 400~ | 22~ | ~175 | 0,46 | 7.7 | 10.5 | 26.4 |
- | 441 | ~0,03 | 17,5~ 18,5 | ~1.0 | - | Si~1.0 Ti 0.1~0.6 Nb 9C+0.3~1.0 | 250 | 430~ 630 | 25~ | ~175 | 0,462 | 7.6 | 10.1 | 27.1 |
444 | 444 | ~0,025 | 17.0~ 20.0 | - | 1,75~ 2,5 | Ti, Nb, Zr 8x(C%+N%)~0,8 | 245~ | 410~ | 20~ | ~230 | 0,427 | 7.75 | 11 | 26.8 |
- | 445NF | ~0,015 | 20.0~ 23.0 | ~0,5 | - | Ti+Nb 10(C+N)~0,6 | 245~ | 410~ | 22~ | ~200 | 0,44 | 7.74 | 10.5 | 23 |
446M | 446M | 0,015 | 25~ 28,5 | ~0,3 | 1,5~2,5 | Ti+Nb 8~(C+N) | 270~ | 430~ | 20~ | ~210 | 0,5 | 7.75 | 11 | 18.84 |
Jenis, Sifat Mekanik, Sifat Fisik
|
||||||||||||||
Jenis | Komposisi kimia (%) | Peralatan mekanis | Properti fisik | |||||||||||
KS(JIS) | POSCO | C | Kr | Ni | Mo | Yang lain | Kekuatan Hasil (0,2%) | Daya tarik | Perpanjangan (%) | Kekerasan (Hv) | Panas Spesifik J/g °C | Berat jenis | Koefisien Ekspansi Termal | Konduktivitas termal |
(N/mm²) | (N/mm²) | W/m·°C | W/m·°C | |||||||||||
(20-100°C) | (100°C) | |||||||||||||
410 | 410 | ~0,15 | 11,5~ 13,5 | - | - | - | 205~ | 440~ | 20~ | 210~ | 0,46 | 7.7 | 9.9 | 24.9 |
- | 410B | ~0,15 | 11,5~ 13,5 | 0,6 | - | - | 205~ | 440~ | 20~ | ~210 | 0,46 | 7.75 | 9.9 | 24.9 |
- | 420N1 | ~0,17 | 12.0~ 14.0 | - | - | N~0,14 | 225~ | 520~ | 18~ | ~218 | 0,46 | 7.75 | 10.3 | 23.8 |
420J2 | 420J2 | 0,26~ 0,4 | 12.0~ 14.0 | - | - | - | 225~ | 540~ | 18~ | ~247 | 0,46 | 7.75 | 10.3 | 23.8 |
Jenis | Komposisi kimia (%) | Peralatan mekanis | Properti fisik | |||||||||||
KS(JIS) | POSCO | C | Kr | Ni | Mo | Yang lain | Kekuatan Hasil (0,2%) | Daya tarik | Perpanjangan (%) | Kekerasan (Hv) | Panas Spesifik J/g °C | Berat jenis | Koefisien Ekspansi Termal | Konduktivitas termal |
(N/mm²) | (N/mm²) | W/m·°C | W/m·°C | |||||||||||
(20-100°C) | (100°C) | |||||||||||||
329J3L | 329J3L | ~0,03 | 21.0~ 24.0 | 4,5~ 6,5 | 2.5~ 3.5 | N 0,08~0,20 | 450~ | 620~ | 18~ | ~320 | 0,4 | 7.8 | 13.7 | 19 |
329LD | 329LD | ~0,03 | 19.0~ 22.0 | 2.0~ 4.0 | 1.0~ 2.0 | N 0,14 ~ 02 | 450 | 620~ | 25~ | ~310 | 0,52 | 7.71 | 13.2 | 16.5 |
Mn 2.0~4.0 |